Bambu Lab PLA Alpine Green Sparkle 3D Printing Filament 1KG
Aesthetics & Visual Properties
Material Type: Aesthetic Composite Polylactic Acid (PLA Sparkle)
Visual Finish: Premium matte base color blended with fine, glittering metallic-like sparkle particles
Layer Line Masking: Exceptionally high (The light diffusion caused by the embedded sparkle particles efficiently masks structural layer lines and minor surface artifacts)
Ideal Applications: Creative designs, arts and crafts, holiday decorations, display prototypes, and cosmetic enclosures
Physical & Mechanical Properties
Filament Diameter: 1.75 mm
Dimensional Tolerance: ±0.03 mm
Net Filament Weight: 1.0 kg (2.2 lbs)
Density: 1.24 g/cm³
Tensile Strength (X-Y): 40 ± 3 MPa
Bending Strength (X-Y): 74 ± 4 MPa
Impact Strength (XY-Toughness): 18.2 ± 1.3 kJ/m²
Heat Deflection Temperature (HDT): 54 °C
Recommended Printing Parameters
Nozzle (Extrusion) Temperature: 190 °C - 230 °C (Recommended baseline: 210 °C - 220 °C)
Heated Bed Temperature: 35 °C - 45 °C
Maximum Printing Speed: ≤ 250 mm/s (Seamlessly matches high-speed PLA printing presets)
Compatible Build Surfaces: Textured PEI Plate, Smooth PEI Plate, Cool Plate (Bambu glue helper recommended for smooth surfaces)
Hardware Compatibility & Nozzle Safety
Package Type: Full Spool Package (Includes 1 x Genuine Bambu Reusable Spool made of durable ABS)
Smart Detection: Built-in active RFID chip automatically syncs exact color, material profile, and optimized speed settings with Bambu Lab AMS systems upon loading.
Nozzle Compatibility: Fully compatible with standard 0.4 mm nozzles. Unlike carbon-fiber or glow-in-the-dark filaments, the micro-sparkle particles are completely non-abrasive and do not cause rapid nozzle wear or clogging.
Storage & Drying Guidelines
Drying Requirements: Blast drying oven at 55 °C for 8 hours, or Bambu X1/P1 series heatbed at 65 °C - 75 °C for 12 hours.
Storage Environment: Keep in a dry box or within the AMS chamber with fresh desiccant packings (< 20% RH) to avoid moisture-induced oozing or stringing.